Proprietary Additive |
N/A
LE's proprietary additives are used exclusively in LE lubricants. Pyroshield Syn Open Gear Grease contains Almasol. Almasol® solid wear-reducing additive is able to withstand extremely heavy loads, chemical attack and temperatures up to 1,900ºF (1,038ºC). It is attracted to metal surfaces, forming a microscopic layer but not building on itself or affecting clearances. Almasol minimizes metal-to-metal contact and the resulting friction, heat and wear. |
LE Modified Timken Test |
N/A
Conclusion The results of the comparative product testing demonstrate the outstanding load-carrying capacity of Pyroshield Syn Open Gear Grease. It outperformed every competitive product that was tested. Pyroshield had a narrower wear scar and a lower block temperature than all the other lubricants. The test blocks of the competitive products experienced higher temperatures as a result of friction due to poor lubrication. The difference is easily visible in the amount of discoloration of the test blocks. |
Pyroshield vs Competitive Open Gear Lubricants LWI |
N/A
Conclusion The graph clearly shows the outstanding preventive wear performance that Pyroshield Syn Open Gear Grease provides as compared to competitive products. Load Wear Index (LWI) is a measure of lubricant's ability to carry a load and minimize wear. The higher the value, the better the lubricant does in preventing wear. |
Recommendations |
N/A
|
Typical Applications |
N/A
|
Asset Reliability Solutions |
N/A Reliability Solution Products |
Customer Testimonials |
N/A
5181 5182 Bentonite Corp 5182 City of Auburndale 5182 CW Estes 5182 Rotary Storyland Playland 5182 Town of Bay Harbor Island |
Note |
N/A 30 lb Pail contains 60 1/2-lb bags |
Thickener Type |
N/A Bentone |
Texture |
N/A Smooth/Tacky |
Color |
N/A Purple |
NLGI Grade as Applied |
N/A 2 |
NLGI Grade in Service |
N/A 2 |
Worked 60 Penetration ASTM D217 |
N/A 275 |
Worked 10K Penetration ASTM D217 |
N/A +14 |
Worked 100K Penetration ASTM D217 |
N/A +28 |
Dropping Point ºC(ºF), ASTM D2265 |
N/A Non-melt |
Flash Point ºC (ºF), ASTM D92 |
N/A 224 (435) |
Viscosity @ 100°C, cSt, ASTM D445 |
N/A 690 |
Viscosity @ 40°C, cSt, ASTM D445 |
N/A 26,180 |
Pour Point °C (°F), ASTM D97 |
N/A 3 (37) |
Oxidation drop in psi @ 100 hrs, ASTM D942 |
N/A 3 |
Corrosion Prevention DI H2O, ASTM D1743 |
N/A Pass |
Timken OK Load lbs, ASTM D2509 |
N/A 90 |
Four-Ball EP Weld Point kgf, ASTM D2596 |
N/A 500 |
Four-Ball EP Load Wear Index kgf, ASTM D2596 |
N/A 116 |
Four-Ball Wear @ 75ºC (167ºF), 1,200 rpm, 40 kgf, 60 minutes, mm wear, ASTM D2266 |
N/A 0.71 |
Water Spray-off % Loss, ASTM D4049 |
N/A <2.0 |
Copper Corrosion 24 hrs @ 100ºC, ASTM D4048 |
N/A 1b |